Influence of the static strain ageing on the ductile-to-brittle transition in C-Mn steel

Ferritic steels for industrial structures have a brittle-ductile transition toughness and impact energy with temperature. Their resistance to the brittle fracture plays an essential role in the safety certification of industrial structures. Nowadays, the performance and the durability are key issues for major players such as EDF. In these approaches ductile-to-brittle transition toughness and impact energy, toughness is predicted from resilience. Several previous studies have shown that the probability of cleavage fracture can be adequately described in brittle plateau by a local approach to fracture. However, these studies assume that the material does not undergo strain aging, which is rarely relevant for low carbon steels and low calmed down. The work consisted firstly to characterize the behavior and secondly to propose a robust and explicit modeling of the observed phenomena. Characterization consisted of performing tensile tests between -150 C and 20 C for several strain rates. A model able to simulate the static aging is identified by implementing an appropriate and systematic strategy. Impact resistance test allows us to build the curve of ductile-to-brittle transition of the material for different conditions to understand and observe the influence of static strain aging on the failure. Finally, the modeling of the brittle fracture has been described for all experimental conditions tested using the model developed and identified in the previous section to predict the transition for different material conditions. (author)