Superplasticity of dispersion-hardened nickel alloy with submicrocrystalline structure

Creators

  • 1. Vsesoyuznyj Inst. Legkikh Splavov, Moscow (Russian Federation)
  • 2. Inst. Problem Sverkhplastichnosti Metallov, Ufa (Russian Federation)

Description

A study is made into mechanical behaviour and microstructure of powder dispersion-hardened heat resisting nickel alloy (Ni-7%Al-10%Cr-6.5%W-1.2%Y2O3) produced by mechanical alloying on working in wide temperature (800-1270 deg C) and strain rate (8.3x10-5 - 1.67x10-1 s-1) ranges. It is revealed that hot working gives rise to submicrocrystalline structure with a grain size of 0.5 μm and to both low temperature and high rate superplasticity. It is shown that the stability of submicrocrystalline structure at high temperatures is due to the presence of yttrium refractory phase particles

Abstract (Russian)

Исследовали механическое поведение и микроструктуру порошкового дисперсно-упрочненного жаропрочного никелевого сплава (Ni-7%Al-10%Cr-6.5%W-1.2%Y2O3), полученного методом механического легирования, при деформировании в широком интервале температур (800-1270 град С) и скоростей (8.3x10-5 - 1.67x10-1 с-1). Установлено, что горячая обработка приводит к формированию субмикрокристаллической структуры с размером зерна 0,5 мкм и как низкотемпературной, так и высокоскоростной сверхпластичности. Показано, что стабильность субмикрокристаллической структуры при высоких температурах обусловлена наличием тугоплавких частиц иттриевой фазы

Additional details

Additional titles

Original title (Russian)
Сверхпластичность дисперсно-упрочненного никелевого сплава с субмикрокристаллической структурой

Publishing Information

Journal Title
Izvestiya Vysshikh Uchebnykh Zavedenij. Chernaya Metallurgiya
Journal Issue
no.2
Journal Page Range
p. 36-41
CODEN
IVUMAX

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
34014576
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
DISPERSION HARDENING; FRACTURES; GRAIN SIZE; HOT WORKING; NICKEL BASE ALLOYS; PLASTICITY; SINTERED MATERIALS; STRAIN RATE; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 1000-4000 K; TENSILE PROPERTIES; YTTRIUM OXIDES
Descriptors DEC
ALLOYS; CHALCOGENIDES; FABRICATION; FAILURES; HARDENING; MATERIALS; MATERIALS WORKING; MECHANICAL PROPERTIES; MICROSTRUCTURE; NICKEL ALLOYS; OXIDES; OXYGEN COMPOUNDS; SIZE; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS; TRANSITION ELEMENT COMPOUNDS; YTTRIUM COMPOUNDS

Optional Information

Notes
11 refs.; 1 tab.; 3 figs.