X-ray structural analysis of plasma sprayed europium oxide

An X-ray structure microanalysis is made for europium oxide powder produced by sintering and plasmic spheroidization for plasma spraying. The technique of concern is shown not to alter chemical composition of the powder. It is stated that a rise in the plasma jet enthalpy while spraying does not result in dissociation of europium oxide and its interaction with the plasma flux. The coating (to 15.2 kWxs/g) is found to have only a high-temperature (monoclinic) europium oxide phase and there appears a low-temperature (cubic) phase with a subsequent increase in the enthalpy. The plasma jet enthalpy increasing the grain size and the crystal lattice c parameter of the sprayed europium oxide are shown to decrease; the a parameter reduces with an enthalpy growth to 16.2 kW s/g and then smoothly increases with the enthalpy further growth. It is noticed that the europium oxide coating does not interact with an aluminium D16 alloy substrate