Superconducting transition and Raman spectrum of Y1Ba2Cu3O/sub 7-//sub x/ prepared by polymeric precursor synthesis
Creators
- 1. Korea Standards Research Institute, P.O. Box 3, Taedok Science Town, Taejon, Chungnam 302-340, Republic of Korea
Description
High-T/sub c/ superconducting Y1Ba2Cu3O/sub 7-//sub x/ bulk samples were prepared by polymeric precursor synthesis. Resistance, x-ray diffraction, and Raman scattering measurements were performed for sample characterization. The bulk specimen exhibited a sharp superconducting transition at 94.5 K with a 10%--90% transition width of 0.5 K. Four Raman active phonon modes were observed at frequences of 150, 337, 440, and 502 cm-1 in the 120--700 cm-1 region
Additional details
Publishing Information
- Journal Title
- Journal of Applied Physics
- Journal Volume
- 65
- Journal Issue
- 6
- Series
- J. Appl. Phys.
- Journal Page Range
- 2563-2565
- ISSN
- 0021-8979
- CODEN
- JAPIA
INIS
- Country of Publication
- United States
- Country of Input or Organization
- United States
- INIS RN
- 20033014
- Subject category
- S36: MATERIALS SCIENCE; S75: CONDENSED MATTER PHYSICS, SUPERCONDUCTIVITY AND SUPERFLUIDITY;
- Resource subtype / Literary indicator
- Numerical Data
- Descriptors DEI
- BARIUM OXIDES; COPPER OXIDES; ELECTRIC CONDUCTIVITY; EXPERIMENTAL DATA; FABRICATION; PHONONS; POLYMERS; RAMAN SPECTRA; TRANSITION TEMPERATURE; TYPE-II SUPERCONDUCTORS; X-RAY DIFFRACTION; YTTRIUM OXIDES
- Descriptors DEC
- ALKALINE EARTH METAL COMPOUNDS; BARIUM COMPOUNDS; CHALCOGENIDES; COHERENT SCATTERING; COPPER COMPOUNDS; DATA; DIFFRACTION; ELECTRICAL PROPERTIES; INFORMATION; NUMERICAL DATA; OXIDES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; QUASI PARTICLES; SCATTERING; SPECTRA; SUPERCONDUCTORS; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT COMPOUNDS; YTTRIUM COMPOUNDS