On texture, corrosion resistance and morphology of hot-dip galvanized zinc coatings

Texture is an important factor which affects the coating properties. Chemical composition of the zinc bath can strongly influence the texture of hot-dip galvanized coatings. In this study, lead content of the zinc bath was changed from 0.01 wt.% to 0.11 wt.%. Specimens were prepared from zinc baths of different lead content and its texture was evaluated using X-ray diffraction. Corrosion behaviour was analyzed by Tafel extrapolation and linear polarization tests. To study the corrosion products of the specimens, salt spray test was employed. Also, the spangle size of the specimens was determined using line intercept method. From the experimental results it was found that (00.2) basal plane texture component would be weakened by increasing the lead content of the zinc and conversely (20.1) high angle pyramidal texture components strengthened. Besides, coatings with strong (00.2) texture component and weaker (20.1) component have better corrosion resistance than the coatings with weak (00.2) and strong (20.1) texture components. In addition, surface morphology would be changed and presence of basal planes decreases at the coating surface due to the increase of lead in the zinc bath. Furthermore, spangle size would be increased by increasing the lead content of the zinc bath. Investigation on the effects of skin pass rolling showed that in this case (00.2) basal texture component and corrosion resistance of the skin passed specimens, in comparison with non-skin passed specimens, have been decreased