The resistance of 20Cr/25Ni steels to carbon deposition. Pt. 4
Creators
- 1. Central Electricity Generating Board, Berkeley (UK). Berkeley Nuclear Labs.
Description
The carbon deposition behaviour of sheet specimens of nine experimental alloys, based on the composition of a 20Cr/25Ni/Nb stabilised steel but containing silicon in the range 0.0 to 2.23 w/o, has been studied. The tests were conducted in an environment of 75% CO/CO2 at 1 atmosphere total pressure at a temperature of 923 K. It was found that the resistance to carbon deposition increased with increasing silicon content. By using two heat treatments, it was shown, for steels containing < or approx. 1.5 w/o Si, that the alloy's surface grain size was a key parameter in determining its response to carbon deposition; fine-grained structures exhibited greater resistance than coarse-grained. At the highest alloy silicon contents (1.8, 2.2 w/o), no effect of grain size was found. The results are interpreted in terms of the ease of formation of protective chromia and silica layers. (orig.)
Abstract (German)
Untersucht wurde die Kohleablagerung auf Blechproben neun verschiedener experimenteller Legierungen (Typ 20Cr/25Ni/Nb) mit Siliciumgehalten zwischen 0,0 und 2,23%. Die Untersuchungen wurden in einem Gasgemisch mit 75% CO, Rest CO2, bei 923 K durchgefuehrt. Aufgrund der Ergebnisse nimmt die Bestaendigkeit gegen Kohleablagerung mit dem Siliciumgehalt zu. Die nach zwei Methoden durchgefuehrte Waermebehandlung zeigt, dass im Falle der Staehle mit maximal etwa 1,5 Gew.% Si die Korngroesse an der Legierungsoberflaeche ein entscheidender Parameter fuer die Kohleablagerung ist: feinkoernige Oberflaechen sind danach widerstandsfaehiger als grobkoernige. Bei den hoechsten verwendeten Siliciumgehalten (1,8 bzw. 2,2%) wurde hingegen kein Einfluss der Korngroesse mehr gefunden. Die Ergebnisse werden damit erklaert, dass die Bildung der schuetzenden Chromoxid- und Siliciumoxidschichten mit unterschiedlicher Leichtigkeit erfolgt. (orig.)Additional details
Additional titles
- Subtitle (English)
- The influence of alloy silicon content
Publishing Information
- Journal Title
- Werkst. Korros.
- Journal Volume
- 38
- Journal Issue
- 5
- Series
- Werkst. Korros.
- Journal Page Range
- 224-229
- ISSN
- 0043-2822
- CODEN
- WSKRA
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 19016979
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- BINARY MIXTURES; CARBON; CARBON DIOXIDE; CARBON MONOXIDE; DEPOSITION; GRAIN SIZE; HEAT TREATMENTS; NIOBIUM ADDITIONS; OXIDES; QUANTITY RATIO; SILICON ADDITIONS; STEEL-NI25CR20; SURFACES; VERY HIGH TEMPERATURE
- Descriptors DEC
- ALLOYS; AUSTENITIC STEELS; CARBON ADDITIONS; CARBON COMPOUNDS; CARBON OXIDES; CHALCOGENIDES; CHROMIUM ALLOYS; CHROMIUM-NICKEL STEELS; CORROSION RESISTANT ALLOYS; CRYSTAL STRUCTURE; DISPERSIONS; ELEMENTS; HEAT RESISTING ALLOYS; HIGH ALLOY STEELS; IRON ALLOYS; IRON BASE ALLOYS; MICROSTRUCTURE; MIXTURES; NICKEL ALLOYS; NONMETALS; OXYGEN COMPOUNDS; SIZE; STAINLESS STEELS; STEELS