The effect of processing and composition on the properties of polylactide–multiwall carbon nanotube composites prepared by solvent casting

This study investigates the effects of processing solvent and filler concentration on the thermal, electrical and mechanical properties of polylactide (PLA)–multiwall carbon nanotube (MWNT) composites. PLA–MWNT composites were prepared by a solvent casting method using two different solvents, chloroform and 1,4-dioxane, in compositions of 0, 0.5, 2 and 5 wt% MWNTs. The dispersion of the MWNTs in PLA was examined using a scanning electron microscope and was found to be improved when 1,4-dioxane was used as the solvent as compared with when chloroform was used. Owing to their better MWNT dispersion, composites prepared using 1,4-dioxane displayed a greater dependence on the MWNT concentration of the thermal, electrical and mechanical properties. Composites prepared using 1,4-dioxane had a greater effect on PLA's decomposition temperature and displayed faster crystallization kinetics than those prepared using chloroform. Not only was the conductivity of 1,4-dioxane prepared composites greater than that of chloroform prepared composites, but also the filler percolation point was observed to be reduced as well (less than 0.5 wt% MWNTs). At 5 wt% MWNT composition, a 31% increase in Young's modulus was observed in 1,4-dioxane prepared composites while a 14% improvement was observed in chloroform prepared composites, as compared with neat PLA. On the basis of the results, it is believed that the chemical interaction between the carboxylated MWNTs and 1,4-dioxane allows for a better dispersion of the MWNTs in PLA