Effect of CeO2 addition on the properties of FeAl based alloy produced by mechanical alloying technique

Iron aluminides based on FeAl is notable for their low materials cost, ease of fabrication and good corrosion, suffixation and oxidation resistance. However, the application based on these unique properties still require the development of Fe-Al based alloy since it shows some drawbacks such as a lack of high temperature strength and low ductility. To improve the mechanical properties of FeAl based alloy, ceria (CeO2) will be added to this compound. FeAl based alloy produced by the mechanical alloying (MA) technique. The developed specimens then assessed with respect to oxidation behaviour in high temperature, scale microstructure and hardness. The surface morphologies of the alloy evaluated and observed using scanning electron microscopy (SEM) with an energy dispersive X-ray spectroscopy (EDX). The phase structures of oxide scale formed on them were identified by X-ray diffraction (XRD). The results found that the FeAl intermetallic compound containing CeO2 0.5 wt.% is less pores and CeO2 1.0 wt.% is more homogen in powder and solid form, higher hardness and increase in their resistance to oxidation behaviour in high temperature compared with another percentage of CeO2