ERD studies of D-ion depth distributions after implantation into some pure metals and alloys

This paper presents a report on experimental results of depth distributions of deuterium ions implanted with 25 keV energy at a fluence interval of (1.2-2.3)·1022 m-2 into samples of pure metals (Cu, Ti, Zr, V, Pd) and diluted Pd alloys (Pd-Ag, Pd-Pt, Pd-Ru, Pd-Rh). The post-treatment depth distributions of deuterium and hydrogen atoms were measured within a few hours after implantation with the use of elastic recoil detection (ERD) analysis. After three months the measurements were repeated. The comparison of the obtained results in both series of studies allowed us to make an important observation of the desorption rates of implanted deuterium atoms from pure metals and diluted Pd alloys. The maximum measured concentrations of deuterium atoms in pure Zr and Ti foils with relatively small desorption rate of deuterium atoms within three months after implantation were observed. Also, a very high spreading of deuterium atom distributions was observed in all the measured pure metals and alloys. It can be explained by the large diffusion coefficients of deuterium and extremely fast kinetics