Corrosion and protection of uranium alloy penetrators

Penetrators made from either a U--3/4 percent Ti alloy or a U--3/4 percent Mo--3/4 percent Zr--3/4 percent Nb--1/2 percent Ti alloy (''Quad'') corrode mildly in moist air, significantly in moist nitrogen, and severely in salt fog. Adequate protection was provided in moist air and nitrogen by coating with electroplated nickel, electroplated nickel and zinc with a chromate finish, and galvanized zinc with a chromate finish. In salt fog, electroplated nickel offered only temporary protection whereas galvanized zinc and electroplated nickel-zinc provided long-lasting protection. The resistance of uncoated penetrators was affected variously by dissimilar metal couplings. Aluminum protected the Quad alloy and adversely affected the U--3/4 percent Ti alloy, whereas steel enhanced localized corrosion in both. (U.S.)