Size-affected single-slip behavior of René N5 microcrystals

Highlights: ► Microcompression testing was conducted on the single crystal superalloy René N5. ► All microcrystals exhibited size-affected plastic flow. ► Dendrite core microcrystals were stronger than those from interdendritic regions. - Abstract: Microcompression testing was conducted on the cast single crystal nickel-base superalloy René N5. Microcrystals were selectively fabricated from either dendrite core or interdendritic regions. The compression axis was oriented for single-slip deformation and microcrystal diameters ranged from 2.5 to 80 μm. All microcrystals displayed several hallmarks of size-affected plastic flow, including a size-affected and stochastic flow-stress and initial strain hardening rate, as well as an intermittent flow response. The magnitude of size-affected flow-stress scaling behavior was dependent upon the plastic strain level of the flow-stress measurement, with increasing size-dependence for increasing strain levels. TEM analysis demonstrated the activation of multiple slip-systems, despite the microcrystals being oriented for single-slip deformation. Zig-zag slip was also observed in microcrystals that achieved flow stresses of ∼1300 MPa or higher. For microcrystals fabricated within interdendritic regions the flow-stress values are, on average, lower compared to dendrite core microcrystals. This difference in flow-stress is especially pronounced for microcrystals which are 5 μm in diameter. The microcrystal diameter for which bulk-like properties are estimated to be observed is approximately 350 μm, which is approaching the measured primary dendrite arm spacing for this crystal (430 μm).