Bio-template-assisted synthesis of hierarchically hollow SiO2 microtubes and their enhanced formaldehyde adsorption performance

The indoor air quality is crucial for human health, taking into account that people often spend more than 80% of their time in houses, offices and cars. Formaldehyde (HCHO) is a major pollutant and long-term exposure to HCHO may cause health problems such as nasal tumors and skin irritation. In this work, for the first time, hierarchically hollow silica microtubes (HHSM) were synthesized by a simple sol–gel and calcination method using cetyltrimethyl ammonium bromide (CTAB) and bio-template poplar catkin (PC) as co-templates and the PC/SiO2 weight ratio R was varied from 0, 0.1, 0.3 and 1. The prepared samples were further modified with tetraethylenepentamine (TEPA) and characterized by scanning electron microscope (SEM), transmission electron microscopy (TEM), Fourier transform infrared (FTIR), X-ray photoelectron spectroscopy (XPS), differential thermal analysis (DTA), thermal gravimetric analysis (TGA), and N2 physisorption techniques. This was followed by formaldehyde adsorption tests at ambient temperature. The results showed that all the prepared HHSM samples contained small mesopores with peak pore size at ca. 2.5 nm and large several tens of nanometer-sized pores on the tube wall. The R exhibited an obvious influence on specific surface areas and the sample prepared at R = 0.3 exhibited highest specific surface area (896 m2/g). All the TEPA-modified samples exhibited enhanced formaldehyde adsorption performance. The maximum HCHO adsorption capacity (20.65 mg/g adsorbent) was achieved on the sample prepared at R = 0.3 and modified by 50 wt.% TEPA. The present study will provide new insight for the utilization of bio-template used for the fabrication of inorganic hollow tubes with high HCHO adsorption performance for indoor air purification.