Americium alloys with gold and copper

Presented are results of the production and X-ray examination of micro-samples of americium-241 compounds with gold and copper produced by high-temperature condensation of metal americium vapor onto corresponding substrates. No mutual solubility of the investigated system components was revealed at room temperature. The following three intermetallic compounds were revealed in the Am-Au system: Au6Am with tetragonal lattice of the Au6Sm structural type, AuAm with orthorhombic lattice of the CuCe structural type and AuAm with cubic lattice. The Am-Cu system showed the intermetallic compound Cu5Am (Cu7Am) with a hexagonal lattice of the Cu5Ca(Cu7Tb) structure type. An effect of the 241Am nuclide alpha-activity on the crystal structure of the produced intermetallide was studied.