Magnetotransport in core-shell Fe-Fe oxide nanostructures

Magnetic and magnetotransport measurements were performed on gas-phase synthesized Fe nanoparticles subjected to surface oxidation and cold consolidation. Two samples were investigated with α-Fe volume fraction of 0.15 and 0.60. The sample with smaller metallic fraction is below the percolation threshold for metallic conduction and the conduction mechanism is dominated by thermally activated processes across the oxide. In this case, by lowering the temperature, an increase of the negative magnetoresistance is observed up to 5% at 50 K in a magnetic field of 70 kOe. The magnetoresistance dependence on the sample magnetization, temperature and sample composition is discussed considering the magnetic correlations present in these nanostrucuterd systems