Solution and precipitation of excess phases and nitrogen partition between solid solution and nitrides in corrosion-resistant steel
- 1. Moskovskij Inst. Stali i Splavov, Moscow (Russian Federation)
Description
Experimental study results on dissolution and precipitation of nitrides during crystallization and heat treatment of high nitrogen austenitic steels are presented. It is established that even on rapid crystallization most of nitrogen is in nitrides, and for their dissolution high temperatures and long-term holding at heat are needed. A nitrogen content in the steel should be optimized according to the structure required (austenite or austenite + excess phases). It is noted that a high nitrogen concentration in the steel is not necessarily efficient to attain a high strength
Abstract (Russian)
Приведены результаты экспериментального исследования растворения и выделения нитридов при кристаллизации и термической обработке высокоазотистых аустенитных сталей. Установлено, что даже при быстрой кристаллизации большая часть азота находится в нитридах, и для их растворения требуются высокие температуры и длительные выдержки. Содержание азота в стали должно быть оптимизировано в соответствии с требуемой структурой (аустенит или аустенит + избыточные фазы). Отмечено, что для достижения высокой прочности высокое содержание азота в стали не всегда эффективноAdditional details
Additional titles
- Original title (Russian)
- Растворение и выделение избыточных фаз и распределение азота между твердым раствором и нитридами в коррозионно-стойкой стали
Publishing Information
- Journal Title
- Metally (Moscow)
- Journal Issue
- no.5
- Journal Page Range
- p. 88-93
- ISSN
- 0869-5733
- CODEN
- MEALET
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 38029628
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CHROMIUM NITRIDES; CONCENTRATION RATIO; CRYSTALLIZATION; METALLURGICAL EFFECTS; MICROHARDNESS; MOLYBDENUM NITRIDES; NITROGEN ADDITIONS; PHASE STUDIES; PRECIPITATION HARDENING; SOLIDIFICATION; SOLUBILITY; STEEL-CR18NI10TI; VANADIUM NITRIDES
- Descriptors DEC
- ALLOYS; AUSTENITIC STEELS; CARBON ADDITIONS; CHROMIUM ALLOYS; CHROMIUM COMPOUNDS; CHROMIUM-NICKEL STEELS; CORROSION RESISTANT ALLOYS; DIMENSIONLESS NUMBERS; HARDENING; HARDNESS; HEAT RESISTANT MATERIALS; HEAT RESISTING ALLOYS; HIGH ALLOY STEELS; IRON ALLOYS; IRON BASE ALLOYS; MATERIALS; MECHANICAL PROPERTIES; MOLYBDENUM COMPOUNDS; NICKEL ALLOYS; NITRIDES; NITROGEN COMPOUNDS; PHASE TRANSFORMATIONS; PNICTIDES; REFRACTORY METAL COMPOUNDS; STAINLESS STEELS; STEELS; TITANIUM ADDITIONS; TITANIUM ALLOYS; TRANSITION ELEMENT ALLOYS; TRANSITION ELEMENT COMPOUNDS; VANADIUM COMPOUNDS
Optional Information
- Notes
- 22 ref., 2 figs., 2 tabs.