Phase stability of cuprate superconductors of NdBa2Cu3Oz composition

Creators

  • 1. Moskovskij Gosudarstvennyj Univ. im. M.V. Lomonosova, Moscow (Russian Federation)

Description

Phase stability of high-tc superconductor Nd1+xBa2Cu3Oz synthesized from high-homogeneous reagents is considered in a wide temperature (600-1100 Deg C) range. It is detected that phase of stoichiometric in cations NdBa2Cu3Oz (x=0) composition having maximal transition temperature to superconducting state (Tc=94 K) can to exist near 985 Deg C (pO2=21280 Pa) only as at higher and lower temperature solid solutions with x≅0.05-0.1 are stable. As a result low-temperature oxidation of NdBa2Cu3Oz (600 Deg C, oxygen) phase can to drive to solid-phase decomposition with barium cuprate formation and considerable decrease of Tc. At 1060-1080 Deg C partial melting and growth of threadlike whisker-crystals take place

Abstract (Russian)

В широком диапазоне температур (600-1100 град C) рассмотрена фазовая стабильность высокотемпературного сверхпроводника Nd1+xBa2Cu3Oz, синтезированного из высокогомогенных реагентов. Обнаружено, что фаза стехиометрического по катионам состава NdBa2Cu3Oz (x=0), обладающая максимальной температурой перехода в сверхпроводящее состояние (Tc=94 K), может существовать лишь около 985 град C (pO2=21280 Па), в то время как при более высоких и более низких температурах устойчивы твердые растворы с x≅0.05-0.1. Как следствие, низкотемпературное окисление фазы NdBa2Cu3Oz (600 град C, кислород) может приводить к твердофазному распаду с образованием купратов бария и существенному понижению Tc, а при температурах 1060-1080 град C происходит частичное плавление и рост нитевидных кристаллов-вискеров

Additional details

Additional titles

Original title (Russian)
Фазовая стабильност' купратных сверхпроводников состава NdBa

Publishing Information

Journal Title
Zhurnal Neorganicheskoj Khimii
Journal Volume
45
Journal Issue
6
Journal Page Range
p. 917-927
ISSN
0044-457X
CODEN
ZNOKAQ

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
31064936
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
BARIUM COMPOUNDS; CHEMICAL COATING; CHEMICAL PREPARATION; CRITICAL TEMPERATURE; CUPRATES; HIGH-TC SUPERCONDUCTORS; NEODYMIUM COMPOUNDS; PHASE STUDIES; SOLID SOLUTIONS; STABILITY; SUPERCONDUCTIVITY; TEMPERATURE RANGE 0400-1000 K; TEMPERATURE RANGE 1000-4000 K
Descriptors DEC
ALKALINE EARTH METAL COMPOUNDS; COPPER COMPOUNDS; DEPOSITION; DISPERSIONS; ELECTRIC CONDUCTIVITY; ELECTRICAL PROPERTIES; HOMOGENEOUS MIXTURES; MIXTURES; OXYGEN COMPOUNDS; PHYSICAL PROPERTIES; RARE EARTH COMPOUNDS; SOLUTIONS; SUPERCONDUCTORS; SURFACE COATING; SYNTHESIS; TEMPERATURE RANGE; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT COMPOUNDS; TRANSITION TEMPERATURE; TYPE-II SUPERCONDUCTORS

Optional Information

Notes
20 refs., 9 figs.