Influence of Nb alloying additives on the solid solubility limit of C in Mo
Creators
- 1. Max-Planck-Institut fuer Metallforschung, Stuttgart (Germany, F.R.). Inst. fuer Werkstoffwissenschaften
Description
The solid solubility limit of C in Mo and Mo-rich Mo-Nb alloy (<= 10 at.% Nb) has been investigated in the temperature range of 1500 to 20600 C. A special C-doping technique with subsequent chemical analysis has been applied. This method enables the saturation concentration to be determined regardless of a partial or complete precipitation of C during cooling. The solid solubility limit of C in Mo is given by log csub(C)sub(,)sub(m)sub(a)sub(x). = 7.02 - 9490/T with csub(C)sub(,)sub(m)sub(a)sub(x) in wt.ppm and T in K. The C solubility is decreased by Nb additions. Due to a change in the equilibrium carbide phase (Mo2C and NbC, respectively) with Nb content and temperature the solid solubility limit of C in Mo-rich Mo-Nb alloys cannot be represented by a uniform system of Arrhenius equations. (orig.)
Abstract (German)
Die Loeslichkeitsgrenze von C in Mo und Mo-reichen Mo-Nb-Legierungen (<= 10 At.-% Nb) wurde im Temperaturbereich 1500 bis 20600C untersucht. Eine spezielle C-Dotierung mit nachfolgender chemischer Analyse erlaubte es, die Saettigungskonzentration zu bestimmen, auch wenn eine teilweise oder vollstaendige Ausscheidung des C erfolgt war. Die Loeslichkeitsgrenze von C in Mo wird durch die Beziehung log csub(C)sub(,)sub(m)sub(a)sub(x) = 7,02 - 9490/T wiedergegeben (csub(C)sub(,)sub(m)sub(a)sub(x) in Gew.-ppm, T in K). Durch Nb-Zusaetze wird die maximale C-Loeslichkeit erniedrigt. Sie kann nicht mehr durch ein einheitliches System von Arrheniusbeziehungen beschrieben werden, weil je nach Nb-Konzentration und Temperatur verschiedene Karbidphasen (Mo2C, NbC) mit dem α-Mischkristall im Gleichgewicht stehen. (orig.)Additional details
Additional titles
- Original title (German)
- Einfluss von Niobzusaetzen auf die Loeslichkeitsgrenze von Kohlenstoff in Molybdaen
Publishing Information
- Journal Title
- Z. Metallkd.
- Journal Volume
- 72
- Journal Issue
- 7
- Series
- Z. Metallkd.
- Journal Page Range
- 490-494
- ISSN
- 0044-3093
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 13650070
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- ARRHENIUS EQUATION; BINARY ALLOY SYSTEMS; CARBON; COOLING; CRYSTAL DOPING; DOPED MATERIALS; MOLYBDENUM; MOLYBDENUM BASE ALLOYS; NIOBIUM ADDITIONS; NIOBIUM ALLOYS; PHASE DIAGRAMS; PRECIPITATION; QUANTITATIVE CHEMICAL ANALYSIS; SATURATION; SOLUBILITY; TEMPERATURE DEPENDENCE; TERNARY ALLOY SYSTEMS; THERMODYNAMICS; VERY HIGH TEMPERATURE
- Descriptors DEC
- ALLOY SYSTEMS; ALLOYS; CHEMICAL ANALYSIS; DIAGRAMS; ELEMENTS; INFORMATION; METALS; MOLYBDENUM ALLOYS; NONMETALS; SEPARATION PROCESSES; TRANSITION ELEMENT ALLOYS; TRANSITION ELEMENTS