Temperature influence on the reaction kinetics of V(IV)/V(V) in methanesulfonic acid for all-vanadium redox flow battery

Highlights: • Diffusion coefficients and standard rate constants of V(IV) and V(V) in MSA at different temperatures are studied. • Carbon-based and metal electrodes are investigated under the same experimental condition at high temperature. • The influence of temperature on reaction kinetics is more significant on carbon-based electrode than metal electrode. • Gold electrode shows inefficient performance in MSA solution. - Abstract: In this study, methanesulfonic acid has been investigated as the supporting electrolyte for vanadium solutions due to the improvement of mass transfer rate and reaction kinetics. Here, we applied different temperatures (0–55 °C) for electrochemical experiments of 0.1 M vanadium ions in 1.0 M MSA electrolyte on gold, platinum and glassy carbon electrodes separately to study the temperature-related kinetics. Considering that electron transfer is the control path for the whole reduction potential window, the rotating disc electrode approach was utilized for the oxidation of V(IV) ions, while the reduction of V(V) ions was studied by cyclic voltammetry. The influence of temperature on charge-transfer resistance and mass transport for both V(IV) and V(V) solutions was studied by electrochemical impedance spectroscopy on glassy carbon electrode. The results showed that the diffusion coefficients in both redox reactions on all electrodes increased with temperature, and most were in the order of 10⁻⁶ cm² s⁻¹. The positive influence of temperature was also observed on the standard rate constants for all conditions in this study, most significantly on the glassy carbon electrode. Comparison between glassy carbon electrode and metal electrodes indicates a promising potential of carbon-based material as electrode for redox flow battery.