Structure and properties of hard tantalum-bearing alloy in partly replacement of tantalum carbide by niobium carbide

Creators

  • 1. VNIITS, Moscow (Russian Federation)

Description

The effect of tantalum carbide replacement by niobium carbide on structure and properties of T5 alloy is studied. 5 variants of T5 alloy were produced and studied with different ratio TaC/NbC. According to metallographic analysis data the samples of some variants possessed a 3-phase structure. Porosity was 0.02 - 0.04 % (vol). Medium grain size of α - (WC) - phase was 2.3 μm and that of γ - (Ti, W, Ta, Nb)C - phase was 2.8 - 3.1 μm. An insignificant tendency towards strength decrease and endurance increase in the process of cutting with increased content of Nb up to 60 % is shown. Nb introduction into T5 alloy > than 50 % is regarded as unsuitable because it considerably decreases its plasticity

Abstract (Russian)

Изучено влияние замены карбида тантала карбидом ниобия на структуру и свойства сплава Т5. Были изготовлены и исследованы 5 вариантов сплава Т5 с различным соотношением TaC/NbC. По данным металлографического анализа, образцы нескольких вариантов имели 3-фазную структуру. Пористость составляла 0.02 - 0.04 % (об). Средний размер зерна α - (WC) - фазы составлял 2.3 мкм и γ - (Ti, W, Ta, Nb)C - фазы - 2.8 - 3.1 мкм. Показана незначительная тенденция к снижению прочности и увеличению стойкости при резании с увеличением содержания Nb до 60 %. Введение Nb в сплав Т5 > 50 % считается нецелесообразным, так как значительно снижает его пластичность

Additional details

Additional titles

Original title (Russian)
Структура и свойства твердого танталосодержащего сплава при частичной замене карбида тантала на карбид ниобия

Publishing Information

Journal Title
Tsvetnye Metally
Journal Issue
no.6
Journal Page Range
p. 67-68
ISSN
0372-2929
CODEN
TVMTAX

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
35001578
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
CONCENTRATION RATIO; GRAIN SIZE; NIOBIUM CARBIDES; PHASE STUDIES; POROSITY; TANTALUM CARBIDES; TENSILE PROPERTIES
Descriptors DEC
CARBIDES; CARBON COMPOUNDS; MECHANICAL PROPERTIES; MICROSTRUCTURE; NIOBIUM COMPOUNDS; REFRACTORY METAL COMPOUNDS; SIZE; TANTALUM COMPOUNDS; TRANSITION ELEMENT COMPOUNDS

Optional Information

Notes
3 refs., 1 tab.