Electromagnetic attenuation analysis of Ni0.4Zn0.6Fe2O4 obtained by citrate precursor method

In this work, two types of synthesized Ni0,4Zn0,6Fe2O4 by citrate precursor method. The first type was calcined at 350 deg C for 3.5 h, and the second, after calcination, it was subjected to heat treatment at 600 deg C for 2h in argon atmosphere. Both types were analyzed by X-ray diffraction (XRD) and equipment waveguide. The data were investigated by Rietveld refinement method and showed the NiZn ferrite phase with crystallite size of 12.2 +- 0.1 nm (350 deg C) and 166.7 +- 3.6 nm (600 deg C). The heat treatment also influenced the values of electric permittivity and magnetic permeability, and attenuation of electromagnetic radiation in the frequency range in microwave (8-12 GHz). The sample treated attenuates more and allows its application with thinner, making it attractive its use as absorber material in this frequency range. (author)