Wear mechanisms of Al2O3/TiC/Mo/Ni ceramic wire-drawing dies

Al2O3/TiC/Mo/Ni ceramic composites were produced by hot-pressing for the use of wire drawing dies. The fundamental properties of these ceramic die materials were examined. Wire drawing tests were carried out on the 65Mn steel wire with these ceramic dies. Finite element method (FEM) was used as a means of numerically evaluating stress and its distribution inside the ceramic drawing dies. Worn bore surfaces of the ceramic drawing dies were examined by scanning electron microscopy (SEM). The wear mechanisms of the ceramic drawing dies were investigated. Detailed observations and analyses of the die wear surface have revealed that the most common failure of the ceramic drawing die is the wear at its approach zone. FEM analysis showed that the compressive stresses on both sides of the corners at the approach zone are higher than those of other parts of the ceramic drawing die. Abrasive and adhesive wear were found to be the predominant wear mechanisms through the whole approach zone owing to the greater compressive stresses. Examination of the center bore surface at the die bearing zone of the ceramic drawing dies demonstrated that the wear occurred by light abrasive, no adhesion wear was observed