Honeycomb structured porous interfaces as templates for protein adhesion

We prepared breath figure patterns decorated with a statistical glycopolymer, (styrene-co-2-{[(D-glucosamin-2-N-yl)carbonyl]oxy}ethyl methacrylate, S-HEMAGl). The preparation of the glycopolymer occurs in one single step by using styrene and S-HEMAGl. Blends of this copolymer and high molecular weight polystyrene were spin coated from THF solutions leading to the formation of surfaces with both controlled functionality and topography. AFM studies revealed that both the composition of the blend and the relative humidity play a key role on the size and distribution of the pores at the interface. The porous films shows the hydrophilic glycomonomer units are oriented towards the pore interface since upon soft annealing in water, the holes are partially swelled. The self-organization of the glycopolymer within the pores was additionally confirmed both by reaction of carbohydrate hydroxyl groups with rhodamine-isocyanate and by means of the lectin binding test using Concanavalin A (Con A).