The influence of thermal and tension loading on the material behaviour of the pressure vessel steel 22 NiMoCr 37
Creators
- 1. Technische Hochschule Aachen (F.R. Germany). Inst. fuer Schweisstechnische Fertigungsverfahren
Description
A description of the photoemission electron microscope (PhEEM) gives a survey on this unusual type of microscope. The thermal and tension loading of the structural steel 22 NiMoCr 37 during weld cladding may lead to intergranular stress relief cracking in the heat-affected zone. The material behaviour of this steel is studied in situ in the PhEEM by a simulated welding of flat tensile test pieces. Stress relief cracking starts with the formation of micropores on the former austenitic grain boundaries. Among other things, the susceptibility to cracking is due to segregation processes of tracer elements and impurities. A model of crack formation interprets structural changes under loading at temperatures from 440 to 6300C as the main cause of interganular microseparations. (orig.)
Abstract (German)
Eine Beschreibung des Photoemissions-Elektronenmikroskop (PhEEM) gibt einen Ueberblick ueber diesen seltenen Mikroskoptyp. Die mit dem Schweissplattieren verbundene Temperatur- und Zugbeanspruchung des Baustahls 22 NiMoCr 37 kann zur Entstehung interkristalliner Risse in der Waermeeinflusszone waehrend des Spannungsarmgluehens fuehren. Das Werkstoffverhalten dieses Stahls wird im PhEEM in situ studiert, indem Flachzugproben eine schweisssimulierende Behandlung erfahren. Das 'stress relief cracking' beginnt mit der Bildung von Mikroporen auf den ehemaligen Austenitkorngrenzen. Fuer die Rissempfindlichkeit sind u.a. Steigerungsvorgaenge von Spuren- und Begleitelementen verantwortlich. Ein Modell der Rissentstehung sieht in den Gefuegevorgaengen unter Last im Temperaturbereich von 440 bis 6300C die Hauptursache fuer die Bildung interkristalliner Mikrotrennungen. (orig.)Additional details
Additional titles
- Original title (German)
- Einfluss von Temperatur- und Zugbeanspruchungen auf das Werkstoffverhalten des Druckbehaelterstahles 22 NiMoCr 37
Publishing Information
- Imprint Title
- VGB conference on materials and welding in power plants 1974 - VGB materials conference 1974
- Imprint Pagination
- p. 97-110.
- Report number
- AED-Conf--74-570-000
Conference
- Title
- VGB conference on materials and welding in power plants - VGB materials conference.
- Dates
- 26 Nov 1974.
- Place
- Duesseldorf, F.R. Germany.
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 7278333
- Subject category
- S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Conference, Non-conventional Literature
- Descriptors DEI
- AUSTENITE; CRACKS; ELECTRON MICROSCOPES; ELECTRON MICROSCOPY; FERRITE; HEAT TREATMENTS; HIGH TEMPERATURE; MARTENSITE; MICROSTRUCTURE; PHOTOEMISSION; PRECIPITATION; RESIDUAL STRESSES; STEEL-22NIMOCR37; TENSILE PROPERTIES; VERY HIGH TEMPERATURE; WELDED JOINTS
- Descriptors DEC
- ALLOYS; ALUMINIUM ADDITIONS; CARBON ADDITIONS; CHROMIUM ADDITIONS; CRYSTAL STRUCTURE; EMISSION; HEAT RESISTING ALLOYS; IRON ALLOYS; IRON BASE ALLOYS; JOINTS; MANGANESE ADDITIONS; MECHANICAL PROPERTIES; MICROSCOPES; MICROSCOPY; MOLYBDENUM ADDITIONS; NICKEL ALLOYS; NICKEL STEELS; SECONDARY EMISSION; SEPARATION PROCESSES; STEELS; STRESSES; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 8 figs.; 7 refs. Available from ZAED. Imprint:VGB-Konferenz Werkstoffe und Schweisstechnik im Kraftwerk 1974 - VGB Werkstofftagung 1974.;Vortraege.