Diaphragms obtained by radiochemical grafting in PTFE

Diaphragms for alkaline water electrolysis are prepared by radiochemical grafting of PTFE fabric with styrene, which is later on sulfonated, or with acrylic acid. The diaphragms obtained are mechanically resistant to potash at temperatures up to 2000C, but show some degrafting, which limits the lifetime. The sulfonated styrene group has been found to be more stable in electrolysis than the acrylic acid. In both cases, the incorporation of a cross-linking agent like divinyl benzene improves the lifetime of the diaphragms. Electrolysis during 500 hours at 1200C and 10 kAm2 could be performed. (author)