Structural-phase transformations during thermal aging and electron irradiation in Fe-35Ni-3Ti alloy
Creators
- 1. Inst. Fiziki Metallov UrO RAN, Ekaterinburg (Russian Federation)
Description
Using the method of scanning tunnel microscopy the processes of formation and growth of γ'-phase precipitates in Fe-35Ni-3Ti alloy are investigated during annealing and 5 MeV electron irradiation. It is shown that irradiation promotes precipitates formation. Both in quenched alloy and in aged at 923 K one, containing near 12 nm size precipitates, irradiation at 573 K results in formation of near 4 nm size precipitates. Formation kinetics corresponds d3 ∼ (Dt) relation, where d3 - diameter of forming precipitates, D - effective coefficient of diffusion, t - time of annealing or irradiation. It is marked that irradiation at 573 K increases diffusion coefficient of 5,5 times as compared to isothermal annealing at this temperature. Thus at irradiation radiation-induced diffusion of Ni and Ti atoms takes place, that agrees with obtained earlier data of Moessbauer study
Abstract (Russian)
Методом сканирующей туннельной микроскопии исследованы процессы образования и роста выделений γ'-фазы в сплаве Fe-35Ni-3Ti при отжигах и при облучении электронами 5 МэВ. Показано, что облучение ускоряет образование выделений. И в закаленном сплаве, и в состаренном при 923 К сплаве, содержащем выделения размером около 12 нм, облучение при 573 К приводит к образованию выделений размером около 4 нм. Кинетика образования выделений соответствует закономерности d3 ∼ (Dt), где d3 - диаметр образующихся выделений, D - эффективный коэффициент диффузии, t - время отжига или облучения. Отмечается, что облучение при 573 К увеличивает коэффициент диффузии в 5,5 раз по сравнению с изотермическим отжигом при этой температуре. Таким образом при облучении реализуется радиационно-индуцированная диффузия атомов Ni и Ti, что согласуется с полученными ранее данными мессбауэровских исследованийAdditional details
Additional titles
- Original title (Russian)
- Структурно-фазовые превращения при термическом старении и облучении электронами в сплаве Фе-35Ni-3Ti
Publishing Information
- Publisher
- Isd-vo TPU
- Imprint Place
- Tomsk (Russian Federation)
- Imprint Title
- VII International scientific conference Radiation-thermal effects and processes in inorganic materials. Proceedings
- Imprint Pagination
- 768 p.
- Journal Page Range
- p. 440-444
- Report number
- INIS-RU--534
Conference
- Title
- 7. international scientific conference radiation-thermal effects and processes in inorganic materials
- Original Conference Title
- VII Mezhdunarodnaya nauchnaya konferentsiya Radiatsionno-termicheskie ehffekty i protsessy v neorganicheskikh materialakh
- Dates
- 2-10 Oct 2010
- Place
- Tomsk (Russian Federation)
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 44066147
- Subject category
- S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Conference
- Descriptors DEI
- AGING; ANNEALING; CORROSION RESISTANT ALLOYS; DIFFUSION; ELECTRON BEAMS; IRON ALLOYS; KINETICS; MEV RANGE 01-10; NICKEL ALLOYS; PHASE STUDIES; QUENCHING; SCANNING ELECTRON MICROSCOPY; SIZE; TEMPERATURE RANGE 0400-1000 K; TITANIUM ALLOYS
- Descriptors DEC
- ALLOYS; BEAMS; ELECTRON MICROSCOPY; ENERGY RANGE; HEAT TREATMENTS; LEPTON BEAMS; MEV RANGE; MICROSCOPY; PARTICLE BEAMS; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 6 refs., 5 figs. Imprint:Trudy VII Mezhdunarodnoj nauchnoj konferentsii Radiatsionno-termicheskie ehffekty i protsessy v neorganicheskikh materialakh