On the possible mechanism of low-temperature strain-induced dissolution of intermetallic phases in FCC Fe-Ni-Ti alloys
Creators
- 1. Inst. Fiziki Metallov UrO RAN, Ekaterinburg (Russian Federation)
Description
Possible mechanisms of strain-induced dissolution of particles in Fe-Ni-Ti austenitic alloys are under consideration. It is shown that the drift of substitution impurity atoms is impracticable at rather low temperatures (77-300 K), but a low-temperature dissolution is liable to proceed due to the drift of interstitial atoms in dislocation fields, these atoms have passed into interstitial positions from the sites of crystal lattice of the particle on deformation
Abstract (Russian)
Рассмотрены возможные механизмы деформационного растворения частиц в аустенитных сплавах Fe-Ni-Ti. Показано, что дрейф атомов примеси замещения при достаточно низких температурах (77-300 К) невозможен, а низкотемпературное растворение может происходить за счет дрейфа в полях дислокаций междоузельных атомов, предварительно перешедших в процессе деформации в междоузельные позиции из узлов кристаллической решетки частицыAdditional details
Additional titles
- Original title (Russian)
- О возможном механизме низкотемпературного деформационного растворения интерметаллидных фаз в Фе-Ни-Ти сплавах с GTsK-решеткой
Publishing Information
- Journal Title
- Fizika Metallov i Metallovedenie
- Journal Volume
- 93
- Journal Issue
- 5
- Journal Page Range
- p. 13-16
- ISSN
- 0015-3230
- CODEN
- FMMEA9
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 34067434
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- ATOM TRANSPORT; DISLOCATIONS; DISSOLUTION; FCC LATTICES; INTERMETALLIC COMPOUNDS; INTERSTITIALS; IRON BASE ALLOYS; NICKEL ALLOYS; PHASE STUDIES; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0065-0273 K; TEMPERATURE RANGE 0273-0400 K; TEMPERATURE RANGE 0400-1000 K; TITANIUM ALLOYS
- Descriptors DEC
- ALLOYS; CRYSTAL DEFECTS; CRYSTAL LATTICES; CRYSTAL STRUCTURE; CUBIC LATTICES; IRON ALLOYS; LINE DEFECTS; NEUTRAL-PARTICLE TRANSPORT; POINT DEFECTS; RADIATION TRANSPORT; TEMPERATURE RANGE; TRANSITION ELEMENT ALLOYS
Optional Information
- Notes
- 22 refs.; 2 tabs.