Furfuryl alcohol as corrosion inhibitor for N80 steel in hydrochloric acid

The ability of furfuryl alcohol (FA) as corrosion inhibitor in controlling corrosion of N80 steel in 15% hydrochloric acid has been investigated. It is found that the percentage inhibition of FA increases almost linearly with its concentration (in the range 10 mM-80 mM) and attains about 91% at 80 mM. FA shows significant inhibition at higher temperatures also (∼82% at 60 deg. C;∼74% at 110 deg. C with 80 mM concentration). FA undergoes acid catalyzed polymerization under the experimental conditions to give polyfurfuryl alcohols (PFA) as evidenced by FTIR and NMR spectral data. Thermodynamic parameters for the corrosion of steel in presence and absence of the inhibitor have been calculated. The inhibitive action may be attributed to adsorption of inhibitor molecules on the active sites of the metal surface following Temkin adsorption isotherm. Potentiodynamic polarization curves indicate that FA acts as mixed type inhibitor. A plausible mechanism for the mode of inhibition has been proposed