Demonstration of leak-before-break in Japan Sodium cooled Fast Reactor (JSFR) pipes

This paper describes the leak-before-break (LBB) assessment procedure applicable to Japan Sodium cooled Fast Reactor (JSFR) pipes made of modified 9Cr–1Mo steel. For the sodium pipes of JSFR, the continuous leak monitoring will be adopted as an alternative to a volumetric test of the weld joints under conditions that satisfy LBB. Firstly, a LBB assessment flowchart eliminating uncertainty resulted from small scale leakage, such as self plugging phenomenon and influence of crack surface roughness on leak rate, was proposed. Secondly, a rational unstable fracture assessment technique, taking the compliance changing with crack extension into account, was also proposed. Thirdly, a crack opening displacement (COD) assessment technique was developed, because COD assessment method applicable to JSFR pipes – thin wall and small work hardening material – had not been proposed yet. In addition, fracture toughness tests were performed using compact tension (CT) specimens to obtain the fracture toughness, JIC, and the crack growth resistance (J–R) curve at elevated temperature. Finally, by using the flowchart, proposed techniques and collected data, LBB assessment for the primary sodium pipes of JSFR was conducted. As a result, LBB aspect was successfully demonstrated with sufficient margins