Static pyrocarbon deposition in the temperature range of 19000C-20000C
Description
By means of static pyrocarbon-depositions, it was the aim to contribute to the understanding of the formation and the deposition of pyrocarbon. To achieve this target, a statistical test programme was applied, which enabled the reduction of the necessary individual trials to only 10 with coincident variation of three independant test-variables. The boundary layer over heated substrates in gaseous atmospheres, the Langmuirzone, was evaluated in various gases by optical means; the structure of the Langmuirzone could be defined. The combination of the results from strcutre evaluations and evaluations from the Langmuirzone let to a better understanding of the pyrolysis procedure; a hypothesis on this subject could be confirmed. A proposal was made to describe the structure of high density pyrocarbon completely. A method for planimetric evaluation of single film exposures was developed and applied. A procedure was also developed for coincident determination of the temperature of two heated objects, and this method could be mathematically verified. (orig.)
Availability note (English)
MF available from INIS under the Report Number.Abstract (German)
Mit Hilfe von statischen Pyrokohlenstoff-Abscheidungen wurde versucht, einen Beitrag zum Verstaendnis der Pyrokohlenstoff-Bildung und -Abscheidung zu erarbeiten. Zur Loesung dieser Aufgabe wurde ein statistisches Versuchsprogramm eingesetzt; die Anzahl der notwendigen Versuche zur Pyrokohlenstoff-Strukturermittlung konnte hiermit auf 10 begrenzt werden bei gleichzeitiger Aenderung dreier unabhaengiger Versuchsvariablen. Die Grenzschicht ueber gluehenden Substraten in Gasatmosphaeren, die Langmuirzone, wurde in verschiedenen Gasen mit optischen Mitteln ausgemessen; der Aufbau der Langmuirzone konnte definiert werden. Die Verknuepfung der Ergebnisse der Struktur-Untersuchungen mit den Messungen an Langmuirzonen fuehrte zu einem besseren Verstaendnis der Pyrolyse-Vorgaenge; eine Hypothese zur Pyrokohlenstoff-Abscheidung konnte erhaertet werden. Ein Vorschlag zur vollstaendigen Beschreibung hochdichter Pyrokohlenstoff-Strukturen wurde vorgelegt. Ein Verfahren zur Planimetrierung von Filmaufnahmen wurde entwickelt und angewandt, ebenso eine Methode zur gleichzeitigen Messung der Temperaturen zweier Strahler; diese Methode wurde ausserdem noch mathematisch begruendet. (orig.)
Files
Restricted
The record is publicly accessible, but files are restricted to users with access.
Additional details
Additional titles
- Subtitle (English)
- Evaluation using a statistical test programme. Optical determination of the deposition-zones
- Original title (German)
- Statische Pyrokohlenstoffabscheidung im Temperaturbereich von 1900
- Original subtitle (German)
- Untersuchungen unter Verwendung eines statistischen Versuchsprogramms. Optische Bestimmungen der Abscheidungszonen.
Publishing Information
- Imprint Pagination
- 192 p.
- Report number
- Juel--1894
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 15066953
- Subject category
- S36: MATERIALS SCIENCE; S36: MATERIALS SCIENCE;
- Resource subtype / Literary indicator
- Thesis
- Descriptors DEI
- CONES; DEPOSITION; GRAPHITE; LABORATORY EQUIPMENT; MICROSTRUCTURE; OPTICAL PYROMETERS; POLYNOMIALS; PRESSURE DEPENDENCE; PYROLYSIS; PYROLYTIC CARBON; REGRESSION ANALYSIS; RESEARCH PROGRAMS; SPACE DEPENDENCE; STATISTICS; SUBSTRATES; SURFACES; TEMPERATURE DEPENDENCE; TEMPERATURE MEASUREMENT; VAPOR DEPOSITED COATINGS; VERY HIGH TEMPERATURE
- Descriptors DEC
- CARBON; CHEMICAL REACTIONS; COATINGS; CRYSTAL STRUCTURE; DECOMPOSITION; ELEMENTS; EQUIPMENT; FUNCTIONS; MATHEMATICS; MEASURING INSTRUMENTS; NONMETALS; PYROMETERS