Experimental and computational approaches to evaluate the environmental mitigation effect in narrow spaces by noble metal chemical addition (NMCA)

The environmental mitigation effect of NMCA in a narrow space was evaluated by experimental and computational approaches. In the experiment at 8 MPa and 553K, T-tube whose branched line had a narrow space was prepared, and the Zr electrodes were set in the branched line at certain intervals, which were 1, 3, 5, 7, 9, 11, 15 and 29 cm from the opening section of the branched line. Electrochemical corrosion potential (ECP) at the tip of the branched narrow space varied in response to the water chemistry in the main line which was at right angle with the branched line. Computational fluid dynamics (CFD) analysis reproduced the experimental results. It was also confirmed by CFD analysis that the ingress of water from the main line into the narrow space was accelerated by cavity flow and thermal convection. By CFD analysis in a thermal sleeve of actual plant condition, which had a narrow space, the concentration of dissolved oxygen at a tip of the thermal sleeve reached at 250 ppb within 300 sec, which was the same concentration of the main line. Noble metal deposition on the surface of the thermal sleeve was evaluated by mass transfer model. Noble metal deposition was the largest near the opening section of the branched line, and gradually decreased toward the tip section. In light of the consumption of dissolved oxygen in the branched line, noble metal deposition in the thermal sleeve was sufficient to reduce the ECP. It was expected that NMCA could mitigate the corrosion environment in the thermal sleeve. (author)