Study of cation diffusion in Zn O using 65Zn as radioactive tracer

Zinc self-diffusion coefficient were measured in polycrystalline Zn O of high purity (99,999%) prepared by conventional sintering at 1393 deg C, 4 h, in oxygen atmosphere. The Zn O samples had high density (>99% of the theoretical density) and grain size of 20 μm. These samples were resintered for 72 h at 1400 deg C in order to increase the grain-size higher than 50 μ m. Samples of 15 x 15 x 2 mm3 were polished with diamond paste, and pre-annealed under the same conditions of temperature and atmosphere of the diffusion annealing. A thin film of 65 Zn - radioactive tracer - applied to the polished surface was oxidized in oxygen atmosphere for a short time before diffusion annealing. The diffusion experiments were performed between 1002 and 1201 deg C in oxygen atmosphere. The 65 Zn diffusion profiles were measured by sectioning in conjunction with residual-activity measurements. The results of the determination of the zinc in Zn O diffusion coefficients in function of temperature are presented and a comparison of these results obtained by the two radioactive method is showed. (author)