Thermal expansivity of highly-stretched linear polyethylene with extended chains irradiated with different doses of γ-rays

Temperature begavior of crystal lattice parameters of highly-stretched samples of linear polyethylene with extended chains irradiated with different doses of γ-rays was studied. It was found that transverse vibrations of macromolecular chains are excited at irradiation doses D≥500 Mrad and temperatures close to the melting temperature of the crystallites. These vibrations cause a sharp increase in the latiice parameter a. But no phase transition to the hexagonal packing occurs. It was shown that the thermal expansivity of the lattice parameter c changes its sign at high irradiation doses. These results are explained by the presence in the crystallites of samples irradiated with large doses of a considerable number of intermolecular chemical bonds