Solid state nuclear magnetic resonance spectroscopy of polymer thin films: chain conformation, dynamics, and morphology

This dissertation presents solid-state NMR studies of the chain conformation, dynamics and morphology of three adsorbed polymer systems: two random semi-crystalline copolymers, poly(ethylene-co-acrylic acid) (PEA) and poly(propylene-co-acrylic acid) (PPA), and an amorphous homopolymer, poly(n-butyl methacrylate) (PnBMA). Zirconia (ZrO2) was chosen as the substrate for all three polymers since the binding of carboxylic acids to this metal oxide is well understood. The choice of polymers was based on their particular bulk conformational and dynamic properties as well as their common use in polymer coatings. These studies are motivated by the general lack of a microscopic picture of adsorbed polymers, which can be provided by NMR, and the relevance of chain conformation and dynamics to important polymer film properties such as adhesion. First the chain conformation and surface binding of adsorbed PEA as a function of acrylic acid content are characterized by 13C cross polarization - magic angle spinning (CP-MAS), 2D1H-13C wideline separation (WISE) and 1H spin diffusion NMR experiments and FTIR-PAS (Fourier transform infrared photoacoustic spectroscopy) measurements. The most important finding is that the chain conformation of adsorbed PEA is determined primarily by the sticker group density rather than the surface coverage. The second study of PEA concerns the chain dynamics in the bulk and adsorbed states. Variable temperature NMR experiments provide evidence that ethylene segments of adsorbed PEA form partially folded loops rather than flat extended trains. Finally 129Xe NMR studies, used to probe the morphology of adsorbed PEA, show a bulk-like signal only for the highest loadings. The second system investigated, PPA, is another semi-crystalline random copolymer which binds to zirconia via carboxylate linkages. The 13C CP-MAS NMR spectra of adsorbed PPAC unexpectedly show splittings normally associated with chain-chain packing in the crystalline regions of bulk polypropylene (PP). The splittings in the spectra of adsorbed PPAC, which are more resolved than in bulk PPA, are proposed to arise from recrystallization of the PP segments between sticker groups. Finally the interfacial properties of an amorphous homopolymer, PnBMA were studied using 13C and 129Xe NMR to characterize adsorbed and filled samples. PnBMA binds to zirconia via the partial hydrolysis of the ester side chains. The remaining ester chains of adsorbed PnBMA are found to segregate to the polymer/air interface. Both adsorbed and ZrO2 filled PnBMA show enhanced local segmental mobility. However, the 129Xe NMR measurements of the filled samples are consistent with restricted motion on a larger length scale which may be due to particle bridging. (author)