In situ corrosion tests on HLW glass as part of a larger approach

In-situ corrosion tests were performed on various candidate high-level waste glasses in the underground laboratory in clay underneath SCK x CEN. The tests exposed the glass samples directly to the Boom clay rock, for maximum durations of 7.5 years. We succeeded to interpret the corrosion data at 90 deg C in terms of dissolution mechanisms, and we concluded that the glass composition has a determining effect on the corrosion stability. The data from our in-situ tests were of high relevance for estimating the long-term behaviour of the glasses. The long-term in-situ tests provide corrosion data which show different trends than other corrosion tests, e.g. shorter duration tests in Boom clay, or tests in deionized water. The initial dissolution rate using MCC1 test at 90 deg C is about the same for the three glasses discussed, but the longest duration in Boom clay at 90 deg C shows a difference in mass loss of about 25 times. We finally present some ideas on how the corrosion tests can meet the needs, such as the modelling of the glass corrosion or providing input in the performance assessment. (author)