The electrochemical polymerization of indole with thiophene

Electropolymerization of indole (IN) in the presence of thiophene (Th) was followed by in situ spectrochemical studies. A correlation between absorbance (390 nm) and charge (at 600 mV) values indicated that oligomeric species were formed in solution, and similar results were found with in situ measurements. The copolymer was characterized by FT-IR, UV-Visible Spectroscopy, Cyclic Voltammetry and four-point probe conductymeter. The increase in conductivity by the incorporation of Th into polyindole was about 60 times for a feed ratio nIN/nTH=1:10 and 19 times for nIN/nTH=1:1. Similar effects were also observed during in situ spectroelectrochemical measurements of copolymer formation. It was also found that the cyclic voltametry peak potentials for the electrogrowth of copolymer films were closely correlated to the conductivities of the corresponding films (measured separately by four-point probe method), thereby allowing us to use the peak potential currents to predict the final copolymer film conductivities during the electrochemical growth process. The ex-situ spectroelectrocopolymerization of indole was also obtained in acetonitril medium.The Tg value of the polymer also increased with the incorporation of Th. The results strongly suggest that IN and Th copolymerize on the electrode surface as well as in solution