Ion nitriding of titanium coatings obtained using liquid-metal carrier

Creators

  • 1. Kubanskij Gosudarstvennyj Tekhnologicheksij Univ., Krasnodar (Russian Federation)

Description

The regularities of nitriding are studied for metal coatings preliminarily deposited from liquid metal medium on a steel 08Kh18N10T surface. The eutectic alloy of Bi-47.3% Pb with 2% of titanium powder is used as a liquid metal medium. It is states that for the titanium-nitrogen layer to have a maximum surface hardness (1400-1600 HV) the process of ion nitriding should be carried out in the nitrogen-hydrogen mixture at 750-800 deg C during 3-7 h at the pressure of 6.65-7.98 h Pa. High microhardness is noted to be attained due to formation of finely dispersed titanium nitrides

Abstract (Russian)

Исследовали закономерности насыщения азотом металлических покрытий, предварительно нанесенных на поверхность стали 08Х18Н10Т из жидкометаллического носителя. В качестве жидкометаллического носителя использовали эвтектический сплав Bi-47,3% Pb с 2% титанового порошка. Установлено, что для получения титано-азотного слоя с максимальной твердостью поверхности (1400-1600 НV) процесс ионного азотирования следует проводить в азотоводородной смеси при 750-800 град. С в течение 3-7 ч при давлении 6,65-7,98 гПа. Высокая микротвердость достигается в результате образования мелкодисперсного нитрида титана

Additional details

Additional titles

Original title (Russian)
Ионное азотирование титановых покрытий, полученных с помощью жидкометаллического носителя

Publishing Information

Journal Title
Metallovedenie i Termicheskaya Obrabotka Metallov
Journal Issue
no.1
Journal Page Range
p. 17-19
ISSN
0026-0819
CODEN
MTOMAX

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
32053985
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
DIFFUSION COATINGS; GLOW DISCHARGES; ION IMPLANTATION; LIQUID METALS; MICROHARDNESS; MICROSTRUCTURE; NITRIDATION; STEEL-CR18NI10TI; SURFACE HARDENING; TEMPERATURE RANGE 1000-4000 K; TITANIUM
Descriptors DEC
ALLOYS; AUSTENITIC STEELS; CARBON ADDITIONS; CHEMICAL REACTIONS; CHROMIUM ALLOYS; CHROMIUM-NICKEL STEELS; COATINGS; CORROSION RESISTANT ALLOYS; ELECTRIC DISCHARGES; ELEMENTS; FLUIDS; HARDENING; HARDNESS; HEAT RESISTANT MATERIALS; HEAT RESISTING ALLOYS; HIGH ALLOY STEELS; IRON ALLOYS; IRON BASE ALLOYS; LIQUIDS; MATERIALS; MECHANICAL PROPERTIES; METALS; NICKEL ALLOYS; STAINLESS STEELS; STEELS; SURFACE TREATMENTS; TEMPERATURE RANGE; TITANIUM ADDITIONS; TITANIUM ALLOYS; TRANSITION ELEMENT ALLOYS; TRANSITION ELEMENTS

Optional Information

Notes
7 refs.; 2 figs.