Effect of TiO₂ nanoporous size on cell viability

Full text: Titanium play an important role in the manufacturing of dental implants. The oxide layer naturally formed on the surface of a titanium device provides biocompatible characteristics, which significantly supports the osseointegration process. It has been supported that a nanostructured TiO₂ surface affects positively the adhesion and proliferation of osteoblasts [1]. A widely technique used for obtaining nanoporous titania is anodizing (or anodic oxidation), which is a non-spontaneous reaction induced by a source of electric current, typically using a solution containing HF [1]. TiO₂ pore diameter can be well controlled in a broad range by adjusting the potentiostatic voltage. J. Park et al. have investigated the development of mesenchymal stem cells on a TiO₂ nanoporous surface and reported a direct relation between the cellular responses with the pore diameter, in the range of 15 - 100 nm [2]. The objective of this work was to investigate deeply the influence of TiO₂ pore diameter in cell viability. Titanium surfaces were anodized by using an electrochemical cell under constant agitation, controlled temperature, and different applied voltages in order to produce different pore diameter, in the nanosize range 15-100 nm. Then, cell proliferation, differentiation, adhesion and viability were investigated in vitro [3]. Surface morphology and chemical composition of the surface treated Ti samples were investigated by SEM, EDS and XPS. The results confirmed the production of a uniform layer of nanoporous TiO₂ with different average porous diameter. The details of sample preparation and the results of cell response tests are going to be presented. [1] S. Minagar et al., Acta Biomat. 8 (2012) 2875; M. Kulkarni et al., Nanotechnology 26 (2015) 062002. [2] J. Park et al., Nano Letters 7 (2007) 1686. [3] G. G. Genchi et al., RSC Adv. 6 (2016) 18502. (author)