Gas metal arc welding in refurbishment of cobalt base superalloys

Refurbishments of superalloys which are used in manufacturing gas turbine hot components usually consists of removing cracks and other defects by blending and then repair welding in order to reconstruct damaged area. In this study, the effects of welding parameters on repair of FSX-414 superalloy, as the most applicable cobalt base superalloy in order to manufacture gas turbine nozzles, by use of Gas Metal Arc Welding (GMAW) technic were investigated. Results then were compared by Gas Tungsten Arc Welding (GTAW). Metallographic and SEM studies of the microstructure of the weld and HAZ showed that there are no noticeable defects in the microstructure by use of GMAW. Also, chemical analysis and morphologies of carbide in both methods are similar. Hardness profile of the GM AW structure then also compared with GTAW and no noticeable difference was observed between the profiles. Also, proper tensile properties, compared with GTAW, can be achieved by use of optimum parameters that can be obtained by examining the current and welding speed. Tensile properties of optimized condition of the GMAW then were compared with GTAW. It was seen that the room and high temperature tensile properties of the GMAW structure is very similar and results confirmed that changing the technic did not have any significant influence on the properties. (paper)