Complete dechlorination of 2,4-dichlorophenol in aqueous solution on palladium/polymeric pyrrole-cetyl trimethyl ammonium bromide/foam-nickel composite electrode

Highlights: ► Pd/PPy-CTAB/foam-Ni electrode with high surface area and low Pd content was prepared. ► The composite electrode was applied to dechlorination of 2,4-DCP in aqueous solution. ► Complete dechlorination of 2,4-DCP was achieved with higher current efficiency. ► Removal efficiency kept 100% after 10 times dechlorination on the stable electrode. ► The electrochemically reductive activation energy was 25.8 kJ mol−1 in this system. -- Abstract: The electrochemically reductive dechlorination of 2,4-dichlorophenol (2,4-DCP) in aqueous solution on palladium/polymeric pyrrole-cetyl trimethyl ammonium bromide/foam-nickel electrode (Pd/PPy-CTAB/foam-Ni electrode) was investigated in this paper. Pd/PPy-CTAB/foam-Ni electrode was prepared and characterized by cyclic voltammetry (CV), scanning electron microscope (SEM), X-ray diffraction (XRD), Brunauer–Emmett–Teller (BET) adsorption and inductively coupled plasma-atomic emission spectroscopy (ICP-AES). The influences of some experimental factors such as the dechlorination current, dechlorination time and the initial pH on the removal efficiency and the current efficiency of 2,4-DCP dechlorination on Pd/PPy-CTAB/foam-Ni electrode were studied. Complete removal of 2,4-DCP was achieved and the current efficiency of 47.4% could be obtained under the conditions of the initial pH of 2.2, the dechlorination current of 5 mA and the dechlorination time of 50 min when the initial 2,4-DCP concentration was 100 mg L−1. The analysis of high performance liquid chromatography (HPLC) identified that the intermediate products were 2-chlorophenol (2-CP) and 4-chlorophenol (4-CP). The final products were mainly phenol. Its further reduction product cyclohexanone was also detected. The electrocatalytic dechlorination pathways of 2,4-DCP on Pd/PPy-CTAB/foam-Ni electrode were discussed. The stability of the electrode was favorable that it could keep dechlorination efficiency at 100% after having been reused 10 times. Results revealed that the stable prepared Pd/PPy-CTAB/foam-Ni electrode presented a good application prospect in dechlorination process with high effectiveness and low cost