Conversion of zircaloy to a massive chemically inert form

The report covers work carried out in the period July 1980 - December 1982 on the development and assessment of an aqueous route for the conversion of Zircaloy fuel element cladding to a stable oxide form and on alternative methods for incorporating the oxide into monolithic waste forms suitable for long-term storage and disposal. The work included two aspects, preliminary process development studies aimed at demonstrating the key steps in the process, and studies on the alternative immobilization techniques and the properties of the resulting waste forms. Experimental studies have shown that the ''hydrous zirconium oxide'' (with a residual fluoride content), following calcination at about 5000C, can be hot-pressed at 800-10000C and 22.5 MPa to a high density ceramic waste form with good capacity for the incorporation of active species, such as U4+ and Sr2+, and high leach resistance. Parallel studies have been carried out on the incorporation of the washed ''hydrous zirconium oxide'' in a range of cement matrices. A preliminary chemical engineering assessment of the overall process has been made and flowsheets for a plant to convert 250 kg Zircaloy/day have been prepared