Formation of non-equilibrium structures in R6M5 steel under strong pulse beams action

Formation of non-equilibrium structures in R6M5 steel surface layer in the supply state under irradiation by strong pulse beams (SPB) is examined. Cylindric samples with diameter 10 mm and height 15 mm of R6M5 fast-cutting steel with following content (weight %): 0.85% C, 0.4% Mn, 0.5% Si, 4.0 Cr; 2.1% V; 5.3% Mo, 6.0% W; 0.4% Ni, Fe (the rest) were examined. Irradiation by SPB was conducted on the 'TEMP' modified accelerator operating in a technological regime with carbon beams parameters: energy from 0.3 up o 0.4 MeV, beam density in an impulse from 20 to 250 A/cm2, pulse duration from 60 tp 100 ns. The beam consists of 70 % carbon ions and 30 % hydrogen ions. Phase identification and its structural phase analysis have been studied on the DRON-3 X-ray diffractometer of common assignment. Topography of metallographic specimen surface has been examined on the REM-200 scanning electron microscope. Doping elements redistribution and phases quantitative characteristics after SPB action were studied with help of the X-ray spectral microanalysis (XRSA) on the MS-46 Camebax microanalyzer. Character of doping elements redistribution in the alloy (XRSA data) show its appreciably redistribution, moreover in the melted zone the increased content of molybdenum, tungsten, vanadium is observing, and in the zone of thermal action its increase relatively to matrix values