Important parameters in sintering of Ta-Hf-carbonitride based hard metals in the presence of reactive liquid phase
- 1. Ljubljana Univ. (Yugoslavia). Fakultet za Naravoslovje in Tehnologijo
- 2. Institut Jozef Stefan, Ljubljana (Yugoslavia)
Description
The sintering behaviour of hard metals, based on HfN or HfN-rich Ta-Hf carbonitrides, bonded by Ni or Co was investigated. During the sintering chemical reactions between binder metal and carbonitride or nitride phase take place which result in the formation of intermetallic compounds. Extensive liquid phase formation could be observed at temperatures above 1,5000C, but limited final density values were obtained, not exceeding 90% of the theoretical value, even after sintering at 1,8000C. Wetting experiments show good wettability of Ta-Hf carbonitride phases by nickel. However, chemical reactions which occur during the experiment do not allow a direct correlation between the sintering ability and wetting behaviour of the system. (orig.)
Abstract (German)
Das Sinterverhalten von auf HfN oder HfN-reichen Ta-Hf Carbonitriden basierenden Hartmetallen, gebunden durch Ni oder Co, wurde untersucht. Waehrend des Sinterns treten chemische Reaktionen zwischen Bindermetall und Carbonitrid- oder Nitridphase auf, die zur Bildung von intermetallischen Verbindungen fuehren. Die weitgehende Bildung von der Fluessigkeitsphase konnte bei Temperaturen ueber 1.5000C beobachtet werden; begrenzte Dichteendwerte, die 90% der theoretischen Werte nicht ueberschreiten, wurden sogar nach Sintern bei 1.8000C gefunden. Benetzungsexperimente zeigen eine gute Benetzbarkeit von Ta-Hf Carbonitridphasen durch Nickel. Chemische Reaktionen, die waehrend des Experimentes auftreten, erlauben jedoch keine direkte Korrelation zwischen der Sinterfaehigkeit und dem Benetzungsverhalten des Systems. (orig.)Additional details
Additional titles
- Original title (no language)
- Aufbau, Herstellung und Eigenschaften hochschmelzender Verbindungen und Systeme (Hartstoffe und Hartmetalle).
Publishing Information
- Imprint Title
- Structure, preparation and properties iof refractory compounds and systems
- Imprint Pagination
- p. 33-41.
- Report number
- KFK-EXT--6/76-1
INIS
- Country of Publication
- Germany
- Country of Input or Organization
- Germany
- INIS RN
- 7270461
- Subject category
- S36: MATERIALS SCIENCE;
- Descriptors DEI
- CERMETS; CHEMICAL COMPOSITION; CHEMICAL REACTIONS; COBALT; DENSITY; DIFFERENTIAL THERMAL ANALYSIS; DROPLETS; HAFNIUM CARBIDES; HAFNIUM NITRIDES; INTERMETALLIC COMPOUNDS; MICROSTRUCTURE; NICKEL; SINTERING; TANTALUM CARBIDES; TANTALUM NITRIDES; WETTABILITY
- Descriptors DEC
- ALLOYS; CARBIDES; CARBON COMPOUNDS; COMPOSITE MATERIALS; CRYSTAL STRUCTURE; ELEMENTS; FABRICATION; HAFNIUM COMPOUNDS; METALS; NITRIDES; NITROGEN COMPOUNDS; PARTICLES; PHYSICAL PROPERTIES; TANTALUM COMPOUNDS; THERMAL ANALYSIS; TRANSITION ELEMENT COMPOUNDS; TRANSITION ELEMENTS
Optional Information
- Notes
- 5 figs.; 1 tab.; 7 refs. Imprint:Aufbau, Herstellung und Eigenschaften hochschmelzender Verbindungen und Systeme (Hartstoffe und Hartmetalle).;Jahresbericht 1975.