Phase transitions of the ZrNiHx hydride
Creators
- 1. Moskovskij Gosudarstvennyj Univ. im. M.V. Lomonosova, Khimicheskij Fakul'tet, Moscow (Russian Federation)
Description
The hydrogen pressure - ZrNiHx hydride composition isotherms were determined under isoplethic experiment conditions during the desorption and sorption of hydrogen. According to the experimental data, the ZrNiHx-H2 system (0 < x < 2.229) experienced two phase transitions, hydrogenolysis with the absorption of large amounts of hydrogen and the reverse transition to the initial state. It was found that the β-phase existed in the ZrNiHx-H2 system at least up to 410 deg C, and the region of its homogeneity was shifted toward the α-solution. The homogeneity region of the γ-phase at 250 deg C on the side depleted of hydrogen extended to the composition x = 1.50, and the temperature of its peritectoid decomposition was above 250 deg C. The hydrogenolysis reaction proceeded with the formation of the ε-ZrH3.153-x - NiZr0.7H0.3x system, which had a much higher (higher by 200-300 torr) partial hydrogen pressure over the temperature range 0-240 deg C, viz., was unstable with respect to the initial system
Abstract (Russian)
Определены изотермы давление водорода - состав гидрида ZrNiHx в условиях изоплетного эксперимента в процессе десорбции и сорбции водорода. На основании экспериментальных данных сделано заключение, что система ZrNiHx-H2, где 0 < x < 2.229, претерпевает два фазовых превращения: гидрогенолиз, протекающий с большим поглощением водорода, и обратное превращение в исходную систему. Для системы ZrNiHx-H2 обнаружено, что β-фаза существует по крайней мере до 410 град С и область ее гомогенности смещена в сторону α-раствора, а область гомогенности γ-фазы при 250 град С со стороны, обедненной водородом, простирается до состава x = 1.50 и температура ее перитектоидного распада выше 250 град С. Отмечено, что в результате реакции гидрогенолиза получается система ε-ZrH3.153-x - NiZr0.7H0.3x, которая в интервале температур 0-240 град С имеет гораздо большее парциальное давление водорода (на 200-300 мм рт. ст.), т.е. является нестабильной по отношению к исходной системеAdditional details
Additional titles
- Original title (Russian)
- Фазовые превращения гидрида ZrNiH
Publishing Information
- Journal Title
- Zhurnal Fizicheskoj Khimii
- Journal Volume
- 81
- Journal Issue
- 10
- Journal Page Range
- p. 1791-1796
- ISSN
- 0044-4537
- CODEN
- ZFKHA9
INIS
- Country of Publication
- Russian Federation
- Country of Input or Organization
- Russian Federation
- INIS RN
- 39023156
- Subject category
- S37: INORGANIC, ORGANIC, PHYSICAL AND ANALYTICAL CHEMISTRY; S36: MATERIALS SCIENCE;
- Descriptors DEI
- CHEMICAL COMPOSITION; DESORPTION; FREE ENTHALPY; HYDROGEN; NICKEL HYDRIDES; PARTIAL PRESSURE; PHASE DIAGRAMS; PHASE TRANSFORMATIONS; PRESSURE DEPENDENCE; PRESSURE RANGE KILO PA; PRESSURE RANGE PA; SORPTION; TEMPERATURE RANGE 0273-0400 K; TEMPERATURE RANGE 0400-1000 K; TEMPERATURE RANGE 1000-4000 K; ZIRCONIUM HYDRIDES
- Descriptors DEC
- DIAGRAMS; ELEMENTS; ENERGY; HYDRIDES; HYDROGEN COMPOUNDS; INFORMATION; NICKEL COMPOUNDS; NONMETALS; PHYSICAL PROPERTIES; PRESSURE RANGE; SORPTION; TEMPERATURE RANGE; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT COMPOUNDS; ZIRCONIUM COMPOUNDS
Optional Information
- Notes
- 15 refs., 4 figs.