Hot-pressed TiB2–10 wt.% TiSi2 ceramic with extremely good thermal transport properties at elevated temperatures (up to 1273 K)

This contribution reports and analyses the high thermal transport property of hot-pressed TiB2–10 wt.% TiSi2 ceramics. Depending on the test temperature, the thermal conductivity values of the TiB2 composite (which range from 89 to 122 W m−1 K−1) are determined to be 18–25% higher than that of monolithic TiB2. The thermal transport properties are analyzed in terms of electronic and phonon contributions. The electronic contribution is the major component of the thermal conductivity of TiB2 and comparable contributions from both electronic and phonon components are observed for the TiB2–TiSi2 composite.