Microstructural aspects of crack formation and propagation in the austenitic steel X6CrNiNb18-10 under low cycle fatigue loading

The understanding of the crack initiation mechanisms and crack growth in apparently monolithic materials like X6CrNiNb18-10 stainless steel under cyclic loading requires the explicit analysis of the phenomena underlying fatigue on both atomistic and microscopic levels. The permanent delivery of mechanical energy through cyclic loading evokes changes in the microstructure that can lead to a martensitic transformation. The transformation of a metastable cubic face centered austenite and formation of a cubic body centered α'-martensite under cyclic loading at room temperature was found, both, in the experiment and in molecular dynamics simulations. The martensite nucleates prevalently at grain boundaries, triple points and at the specimen free surface and forms small (∝ 1 μm) differently oriented grains, also in the same parent austenitic grain. By a combination of interrupted low cycle fatigue tests (LCF) and electron backscatter diffraction (EBSD) measurements the martensitic transformation and subsequent fatigue crack formation were observed at the same area in the microstructure at different stages of the specimen lifetime. The EBSD measurements showed the following crack initiation scenarios: Cracks started (a) at the phase boundary between austenite and α'-martensite, (b) inside fully martensitic areas in the matrix, (c) at broken or debonded coarse NbCs. It is obvious that formation of a hard α'-martensite in a ductile and soft austenite and forming two-phase material causes a heterogeneous stress and strain distribution on the microscopic level. α'-martensite enhances locally the stress amplitude whereas in a soft austenite the plastic strain amplitude increases. Strain concentration in the austenite along the phase boundary is connected with a stress increase along the interface and can initiate fatigue crack there. Also at the crack tip, a permanent martensitic transformation occurs, so that the growth of the fatigue cracks at room temperature seems to be totally controlled by α'-martensite.