Addition of electric arc furnace dust in hot metal changing the form of addition

This research aims to study the incorporation of the mass of electric arc furnace dust (EAFD), by addition in hot metal (1.78% Si) at a temperature of 1,400 degrees Celsius. The EAFD is from a steel plant producing long steel. The addition of the EAFD was as received, in the form of briquettes without agitation of the hot metal and in the form of briquettes with agitation of the hot metal. Previously, the EAFD was characterized using the following techniques: chemical analysis, size analysis, X-ray diffraction, scanning electron microscopy (SEM) and energy dispersive spectroscopy (EDS) microanalysis. The achievement of fusion experiments in laboratory scale, took place in a vertical tubular furnace with temperature control. The fusion experiments to assess the incorporation of EAFD mass used graphite crucibles. After cooling, the hot metal and the slag, remaining in the crucible, were weighed to do a mass balance. A flow of inert gas (argon) was maintained inside the furnace during the experiments. Results show that the experiment with addition of EAFD as received presents the best result of incorporating the mass of the final hot metal (1.73%) combined with the lowest percentage of volatilized mass of EAFD (46.52%). The experiment addition of EAFD in the form of briquette with agitation of hot metal presents the lowest percentage of slag mass (4.58%). The zinc content of volatilized EAFD (64.30%) is higher than the zinc content of the imported ore concentrate (52%) and zinc content of the national ore concentrate (12% to 39%). The presence of lead and cadmium in the slag characterizing it as a hazardous solid waste. (author)