Mechanism of luminescent emission in BaY2F8 scintillators doped with rare earths

In this work samples of Barium Yttrium Fluoride (BaY2F8-BaYF) doped with different concentrations of Tb3+, Er3+, Tm3+ e Nd3+ ions were characterized, aiming their application in radiation detection devices using their scintillating properties. Two types of samples were produced, polycrystalline samples, obtained via solid state reaction and single crystals, obtained via the floating zone melting method. The radioluminescence measurements (RL) revealed that the samples doped with 2.0 or 3.0 % Tb showed RL intensity at 545 nm two times higher than samples of CsI:Tl, although the total scintillation yield was smaller when compared to this commercial scintillator. Thermoluminescence (TL) results showed that all doped samples exhibited the same peak at 123°C, which is characteristic of the matrix (BaY2F2). Comparison of the areas under the TL and RL curves for Tb3+ and Nd3+ doped BaYF revealed that the trapping centers are competing with the scintillation of the samples. However, this was not true for the Er3+ and Tm3+ doped samples and it was found that the scintillation yield is independent of the trap concentration up to a certain concentration limit. From this point on, the scintillation yields started increasing as the trap concentration increased. The radiation damage defects in BaYF:Tb3+ were studied via optical absorption (OA) and correlated with TL, showing that trapping centers are connected to the color centers. All samples exhibited different luminescence decay processes with time constants ranging from microseconds, for the fast processes, milliseconds, for the intermediate ones, and phosphorescent processes with decay time on the order of seconds. For the Nd3+ doped samples, very fast decay process was also found with time constants of about 60ns and that is an indication that this material can be used in fast detection systems, although its scintillation efficiency was weak. The combined results obtained with these techniques together with an analysis of X-ray absorption spectroscopy (XAS) and X-rays Excited Optical Luminescence (XEOL) allowed the development of a model for the scintillation mechanism for the rare earth doped BaYF systems. (author)