Superconducting properties of the atomically disordered compound MgCNi3

Creators

  • 1. UrO RAN, Inst. Fiziki Metallov, Ekaterinburg (Russian Federation)
  • 2. Kitajskaya Akademiya Nauk, Inst. Fiziki, Natsional'naya Lab. Sverkhprovodimosti, Beijing (China)

Description

The influence of disordering induced by reactor irradiation (fast neutron fluence Φ=5x1019 sm-2, Tirr = 340 K) on electrical resistance ρ, superconducting transition temperature TC and the second critical field HC2 is studied using polycrystalline MgCNi3 specimens. It is revealed that TC decreases from 6.5 down to 2.9 K under irradiation and is completely restored on annealing at a temperature of 600 Deg C. The temperature dependences ρ(T) are typical for compounds with a strong electron-phonon interaction. The behaviour of dHC2/dT points to a considerable decrease of electron state density at Fermi level N(EF) on disordering

Abstract (Russian)

Исследовано влияние разупорядочения, индуцированного облучением в ядерном реакторе (флюенс быстрых нейтронов Φ=5x1019 см-2, Tобл.= 340 K), на электросопротивление ρ, температуру сверхпроводящего перехода ТС и второе критическое поле НС2 поликристаллических образцов MgCNi3. Обнаружено, что ТС уменьшается при облучении от 6.5 до 2.9 К и полностью восстанавливается после отжига при температуре 600 град С. Температурные зависимости ρ(T) характерны для соединений с сильным электрон-фононным взаимодействием. Поведение dHC2/dT указывает на значительное уменьшение плотности электронных состояний на уровне Ферми N(EF) при разупорядочении

Additional details

Additional titles

Original title (Russian)
Сверхпроводящие свойства атомно-разупорядоченного соединения MgCNi

Publishing Information

Journal Title
Fizika Metallov i Metallovedenie
Journal Volume
95
Journal Issue
4
Journal Page Range
p. 28-32
ISSN
0015-3230
CODEN
FMMEA9

INIS

Country of Publication
Russian Federation
Country of Input or Organization
Russian Federation
INIS RN
35021934
Subject category
S36: MATERIALS SCIENCE;
Descriptors DEI
CARBON ADDITIONS; CUBIC LATTICES; ELECTRIC CONDUCTIVITY; ENERGY-LEVEL DENSITY; FAST NEUTRONS; MAGNESIUM ALLOYS; NEUTRON FLUENCE; NICKEL ALLOYS; ORDER-DISORDER TRANSFORMATIONS; PHYSICAL RADIATION EFFECTS; POLYCRYSTALS; SINTERED MATERIALS; SUPERCONDUCTORS; TEMPERATURE DEPENDENCE; TEMPERATURE RANGE 0000-0013 K; TRANSITION TEMPERATURE
Descriptors DEC
ALLOYS; BARYONS; CRYSTAL LATTICES; CRYSTAL STRUCTURE; CRYSTALS; ELECTRICAL PROPERTIES; ELEMENTARY PARTICLES; FERMIONS; HADRONS; MATERIALS; NEUTRONS; NUCLEONS; PHASE TRANSFORMATIONS; PHYSICAL PROPERTIES; RADIATION EFFECTS; TEMPERATURE RANGE; THERMODYNAMIC PROPERTIES; TRANSITION ELEMENT ALLOYS

Optional Information

Notes
18 refs.; 4 figs.