Electron Trap Energy Distribution in ALD Al2O3, LaAl4Ox, and GdyAl2-yO3 Layers on Silicon

The energy distribution of electron trap density in atomic layer deposited Al2O3, LaAl4Ox and GdyAl2-yO3 insulating layers was studied by using the exhaustive photodepopulation spectroscopy. Upon filling the traps by electron tunneling from Si substrate, a broad energy distribution of trap levels in the energy range 2–4 eV is found in all studied insulators with trap densities in the range of 1012 cm−2eV−1. The incorporation of La and Gd cations reduces the trap density in aluminate layers as compared to Al2O3. Crystallization of the insulator by the post-deposition annealing is found to increase the trap density while the energy distribution remains unchanged. The similar trap spectra in the Al2O3 and La or Gd aluminate layers suggest the common nature of the traps, probably originating from imperfections in the AlOx sub-network.