Residual Stress Analysis of Severe Plastic Deformed Materials using the Finite Element Method and the Neutron Diffraction Method

Severe plastic deformation (SPD) is one of the most promising top-down techniques, moving towards industrialization to fabricate bulk ultrafine grain materials. The strain distribution and deformation behavior during the ECAP (equal channel angular pressing), influenced by tool angles, friction and material behavior, was studied through experimental and numerical analyses. The residual stress of work piece which was straight before ECAP produces many serious problems in the next processing e.g. input of the work piece for the next ECAP. The bent work piece needs additional straightening or surface polishing even if the amount of bending is small, and residual stress need to be released before service applications. Residual stress, particularly tensile residual stress can be a very important factor in affecting the reliability and integrity of working parts. The formation of tensile residual stress may result in initiation of fatigue cracks, stress corrosion cracking, or other types of fracture. Hence, residual stress and resulting bending need to be controlled during ECAP. Thus, in current study the bending behavior and the residual stress of the work piece in ECAP are analyzed through experimental and finite element analyses by considering the effects of material, geometric, and processing parameters individually. The stress states in the ECAP processed work piece were measured by the non-destructive way using neutron diffraction. Efforts were made to suggest the alternate routes to reduce the residual stress and bending of work piece in ECAP